X120mn Mn12 High Manganese Steel Plate

• After-sales Service: Good
• Warranty: 5 Years
• Type: Steel Plate
• Standard: ASTM, AISI, GB, JIS, DIN, BS
• Surface Treatment: Mill Finish
• Technique: Hot Rolled
• Model NO.: K700, Mn13, X120Mn12, 1.3401, A128, etc
• Application: Ship Plate, Boiler Plate, Container Plate, Flange Plate
• Special Use: Wear Resistant Steel
• Stock: Stock
• Mtc: Mill Test Certificate Can Be Supplied
• Inspection: The Third Party Inspection Canbe Accepted
• Delivery: Immediately Delivery From Stock
• Mill: Baosteel, Tisco, etc
• Transport Package: Standard Export Package: Iron Pallets with Waterpr
• Specification: ISO, BV, SGS, etc.
• Trademark: TISCO, BAO STEEL, POSCO, JISCO, LISCO
• Origin: Shanxi Tisco
• HS Code: 72254099
• Production Capacity: 1000tons/Week

Product Description

X120Mn12 Steel Plate
Commodity
Hot rolled steel a128 high manganese steel plate
Standard
ASTM A128, GB, EN10025
Material
X120Mn12, Mn13, A128, 1.3401 etc
Thickness
2mm-300mm
Width
1000-3000mm
Length
1000-12000mm
Packing
Bundle, kraft paper
Payment term
T/T, L/C
Delivery time
15-20 days, according to the order

Chemical composition (%)
Grade
C
Si
Mn
P
S
Mn13
0.90-1.20
0.30-0.80
11.00-14.00
≤ 0.035
≤ 0.030
Mechanical properties

Grade
Tensile Strength
RM(Mqa)
Reduction
Of area A(%)
Impact property 20° C
Initial hardness value(HB)
Hardness value after hardnening(HB)
Mn13
≥ 800MPa
≥ 40%
Ak≥ 90(J)
200-250
>300


X120Mn12(Mn13)is the best choice for resist-high impact, the material of big stress in Wear resistance. The high manganese steel have two biggest features: One is external impact More bigger, the wear-resistance of appearance is more higher; Another is with the gradually Abrasion of densified laminated appearance, new densified laminated process is formed continually.

Mn13(X120Mn12)wroughtsteel plate have wonderful abrasion resistance of high impact abrasion And big stress abrasion, when using it will not appear crash. It also has the excellence of easy for Cutting, welding, curving and other mechanical properties for process. The traditional used high Chrome forging only have the good wear-resistance of moving abrasion.
Mn13(X120Mn12 rolled plate is reduced the cost of useing for quick wear part of low equipment And save the overhaul fee of equipment, so it improves the competition.