K700 Wear Resistant High Manganese Steel Plate

• Customization: Available
• Type: Steel Plate
• Standard: ASTM, AISI, GB, JIS, DIN, BS
• Model NO.: K700, Mn13, X120Mn12, 1.3401, A128, etc
• Surface Treatment: Mill Finish
• Technique: Hot Rolled
• Application: Ship Plate, Boiler Plate, Container Plate, Flange Plate
• Special Use: Wear Resistant Steel
• Mtc: Mill Test Certificate Can Be Supplied
• Inspection: The Third Party Inspection Canbe Accepted
• Delivery: Immediately Delivery From Stock
• Mill: Baosteel, Tisco, etc
• Transport Package: Standard Export Package: Iron Pallets with Waterpr
• Specification: ISO, BV, SGS, etc.
• Trademark: TISCO, BAO STEEL, POSCO, JISCO, LISCO
• Origin: Shanxi Tisco
• Production Capacity: 1000tons/Week

Product Description

K700 Wear Resistant High Manganese Steel Plate

Standard: ASTM A128, GB, EN10025
Material: K700,X120Mn12, Mn13, A128, 1.3401 etc
Thickness: 2mm-300mm
Width: 1000-3000mm
Length: 1000-12000mm
Packing: Bundle, kraft paper
Payment term: T/T, L/C
Delivery time:Immediately delivery from stock

 X120Mn12(Mn13)is the best choice for resist-high impact, the material of big stress in Wear resistance. The high manganese steel have two biggest features: One is external impact More bigger, the wear-resistance of appearance is more higher; Another is with the gradually Abrasion of densified laminated appearance, new densified laminated process is formed continually.

Mn13(X120Mn12)wroughtsteel plate have wonderful abrasion resistance of high impact abrasion And big stress abrasion, when using it will not appear crash. It also has the excellence of easy for Cutting, welding, curving and other mechanical properties for process. The traditional used high Chrome forging only have the good wear-resistance of moving abrasion.

Mn13(X120Mn12 rolled plate is reduced the cost of useing for quick wear part of low equipment And save the overhaul fee of equipment, so it improves the competition.
 

Grade	C	Si	Mn	P	S
Mn13	0.90-1.20	0.30-0.80	11.00-14.00	≤0.035	≤0.030

Mechanical properties

Grade	Tensile   Strength Rm(Mqa)	Reduction  of area A(%)	Impact  property 20 °C	Initial hardness  value (HB)	Hardness value   after hardnening (HB)
Mn13	≥800MPa	≥40%	ak ≥ 90(J)	200-250	>300